Name |
Weight (g/m2) |
Resin Content(wt%) |
Total Weight(g/m2) |
Formed Thickness(mm) |
Type of Carbon Fiber |
Width of Preimpregnated Cloth(mm) |
YJ-B1K-P125 |
125 |
40 |
208 |
0.138 |
1K |
1000 |
YJ-B3K-T125 |
200 |
40 |
333 |
0.221 |
3K |
1000 |
YJ-B3K-P125 |
200 |
40 |
364 |
0.245 |
3K |
1000 |
YJ-B6K-P125 |
380 |
38 |
613 |
0.403 |
6K |
1000 |
YJ-B6K-T125 |
330 |
38 |
550 |
0.364 |
6K |
1000 |
YJ-B12K-P125 |
740 |
38 |
1210 |
0.794 |
12K |
1000 |
Weight |
Tensile Strength |
Tensile Modulus |
Bending Strength |
Bending Modulus |
Compression Strength |
Compression Modulus |
Cutting Strength |
|||||||
g/m2 |
kgf/mm2 |
MPa |
103kgf/mm2 |
GPa |
kgf/mm2 |
MPa |
103 kgf/mm2 |
GPa |
kgf/mm2 |
MPa |
103 kgf/mm2 |
GPa |
kgf/mm2 |
MPa |
200 |
95 |
930 |
8 |
75 |
90 |
880 |
7 |
65 |
97 |
65 |
7 |
65 |
8 |
80 |